WIRE ROD
Aluminium Wire Rod – EC/Alloy 6201/T4/Deoxi Rod(Sizes – 6.5/7.6/9.5/12.6mm):
Aluminum rod for electrical purposes meets or exceed the following ASTM specifications :
B211-Aluminum and Aluminum Alloy Bar, Rod and Wire
B233-Aluminum Rod, 1350-H12, 1350-H14, 1350-H16 Drawing Stock.
B398-Aluminum Alloy 6201 Drawing Stock.
B531-Aluminum Alloy 5005 Drawing Stock.
B800-Standard Specification for 8000 Series
We manufacture aluminium rod according to all international standards (BS, DIN, IEC, NFC etc) upon request.
The following are the principal products being marketed :
EC1350-Rod with conductivity in a range of 61 % to 63% IACS, and from 60 N/mm2 Up to 150 N/mm2.
5005-Rod with a minimum conductivity of 53.8% IACS, and from 95 N/mm2 up to 200 N/mm2.
6101-Rod with a conductivity of 50.5% up to 53% IACS, and from 160 N/mm2 Up to 220 N/mm2.
KJV’s continuous casting line also features continuous heat-treated 6101 rod.
6201-Rod with a conductivity of 50.5% up to 52.0% IACS, and from 170 N/mm2 Up to 230 N/mm2.
8017-Rod with a minimum conductivity of 58.5% up to 60.8% IACS, and from 115 N/mm2 to 140 N/mm2.
Wire Rod Alloy – Mechanical Aluminum Alloy Rod :
Aluminum rod for mechanical purposes meets or exceeds the following ASTM specifications :
3003 B-211 Aluminum and Aluminum Alloy Bar, Rod and Wire.
5052 B-211 Aluminum and Aluminum Alloy Bar, Rod and Wire.
B-316 Aluminum and Aluminum Alloy Rivet and Cold Heading Wire and Rods.
5056 B-211 Aluminum and Aluminum Alloy Bar, Rod and Wire.
5154 B-211 Aluminum and Aluminum Alloy Bar, Rod and Wire.
6061 B-221 Aluminum and Aluminum Alloy Extruded Bars, Rods, Wire, Shapes and Tubes.
6063 B-221 Aluminum and Aluminum Alloy Extruded Bars, Rods, Wire, Shapes and Tubes.
Wire Rod Deoxi – (Aluminum Continuous Cast Rod) :
Non-heat-treatable alloy
Principle alloying elements : none
(primary trace elements : magnesium, iron and silicon)
Standard diameter : 9.5mm, 12.6 mm. (Tolerance +/- 0.5 mm)
Standard Packaging Weight : As per customer need
Option : Palletized, eye vertical or horizontal
Rod surface condition : very clean to oiled
End – Use Application
General Information :
In the pursuit of correct steel chemistry, temperature and the maximum removal of sulphur, phosphorus and dissolved gases, the single most important step is the deoxidation of steel.
Advantages Of Rod :
- Ease of addition
- Rapid rate of reaction
- Low cost
- Strong affinity for oxygen
- Grain refinement properties